Induction forming and curing of thermoset composite charges

ABSTRACT

A first tooling die and a second tooling die are movable with respect to each other. The first tooling die and the second tooling die form a die cavity. The first tooling die and the second tooling die comprise a plurality of stacked metal sheets. A plurality of air gaps is defined between adjacent stacked metal sheets. A first smart susceptor material is within the die cavity and connected to the first tooling die. The first smart susceptor material has a first Curie temperature. A second smart susceptor material is within the die cavity and associated with the second tooling die. The second smart susceptor material has a second Curie temperature lower than the first Curie temperature. A flexible membrane is between the second tooling die and the first smart susceptor material. The flexible membrane is configured to receive pressure.

CROSS-REFERENCE TO RELATED APPLICATION

This application is a divisional application of U.S. application Ser.No. 15/713,424, entitled “Induction Forming and Curing of ThermosetComposite Charges,” filed Sep. 22, 2017, the entirety of which isincorporated herein by reference.

BACKGROUND INFORMATION 1. Field

The present disclosure relates generally to induction tooling, and morespecifically, to induction tooling for performing manufacturingoperations on thermoset composite charges. Yet more specifically, thepresent disclosure relates to an induction system configured to bothform and cure a thermoset composite charge.

2. Background

Composite materials are tough, light-weight materials created bycombining two or more functional components. For example, a compositematerial may include reinforcing fibers bound in a polymer resin matrix.The fibers may be unidirectional or may take the form of a woven clothor fabric. The fibers and resin are arranged and cured to form acomposite material.

Thermoset composite materials are composite materials having a resinthat cures upon application of at least one of temperature or pressure,thus forming the final composite structure. Thermoset compositematerials are shaped prior to curing.

In manufacturing composite structures, layers of composite material arelaid up. The layers may be comprised of fibers in sheets. These sheetsmay take the form of fabrics, tape, tows, or other suitable forms. Insome cases, resin may be infused or pre-impregnated into the sheets.These types of sheets are commonly referred to as prepreg.

In some examples, thermoset composite structures with complexcross-sections are formed by laying up the complex cross-section layerby layer by hand or using automated lamination equipment such as a tapelaminating machine or a fiber placement system. However, laying upcomplex cross-sections layer by layer may take an undesirable amount oftime. Laying up complex cross-sections layer by layer may impact atleast one of the amount of manufacturing time for a component, theamount of in-process flow time for a layup tool, or the amount of humanoperator time.

Thermoset composite structures with complex cross-sections may becreated by forming thermoset composite charges. A thermoset compositecharge has multiple layers of thermoset prepreg laid up substantiallyflat. A thermoset composite charge may be laid up flat by a tapelaminating machine.

After laying up a thermoset composite charge, the thermoset compositecharge may be drape-formed to a complex cross-section. Drape forminguses a forming tool operating at a forming temperature. After drapeforming, the formed thermoset composite charge is transferred to a curetool, such as an autoclave. Separate forming and curing steps may impactoverall manufacturing time by adding transfer processes. Additionally,separate forming and curing steps use separate forming and curingtooling.

Therefore, it would be desirable to have a method and apparatus thattake into account at least some of the issues discussed above, as wellas other possible issues. For example, it may be desirable to provide anapparatus and method for forming thermosets with complex cross-sectionswith at least one of reduced manufacturing time, reduced manufacturingcosts, or reduced utilities. As another example, it may be desirable toprovide an apparatus for both forming and curing a thermoset compositecharge.

SUMMARY

An illustrative embodiment of the present disclosure provides aninduction system configured to provide temperature and pressure controlfor forming and curing of a thermoset composite charge. The inductionsystem comprises a first tooling die and a second tooling die, a firstsmart susceptor material, a second smart susceptor material, and aflexible membrane. The first tooling die and the second tooling die aremovable with respect to each other. The first tooling die and the secondtooling die form a die cavity. The first tooling die and the secondtooling die comprise a plurality of stacked metal sheets. A plurality ofair gaps is defined between adjacent stacked metal sheets. The firstsmart susceptor material is within the die cavity and connected to thefirst tooling die. The first smart susceptor material has a first Curietemperature. The second smart susceptor material is within the diecavity and associated with the second tooling die. The second smartsusceptor material has a second Curie temperature lower than the firstCurie temperature. The flexible membrane is between the second toolingdie and the first smart susceptor material. The flexible membrane isconfigured to receive pressure.

Another illustrative embodiment of the present disclosure provides aninduction system configured to provide temperature and pressure controlfor forming and curing of a thermoset composite charge. The inductionsystem comprises an induction tool and a conformable smart susceptorblanket positioned within a die cavity of the induction tool. Theinduction tool comprises a first tooling die and a second tooling die, afirst set of conductors, a first smart susceptor surface, and a secondsmart susceptor surface. The first tooling die and the second toolingdie are movable with respect to each other. The first tooling die andthe second tooling die comprise a plurality of stacked metal sheets. Aplurality of air gaps is defined between adjacent stacked metal sheets.The first smart susceptor surface is connected to the first tooling die.The second smart susceptor surface is connected to the second toolingdie.

A further illustrative embodiment of the present disclosure provides amethod. A thermoset composite charge is placed within a die cavity of aninduction tool, wherein the induction tool comprises a first tooling dieand a second tooling die movable with respect to each other, wherein thefirst tooling die and the second tooling die form the die cavity, thefirst tooling die and the second tooling die comprising a plurality ofstacked metal sheets, a plurality of air gaps defined between adjacentstacked metal sheets. The thermoset composite charge within the diecavity is heated to a forming temperature using a second smart susceptormaterial within the die cavity. The thermoset composite charge withinthe die cavity is moved towards a first smart susceptor surfaceconnected to the first tooling die after heating the thermoset compositecharge to the forming temperature. Pressure is applied to the thermosetcomposite charge using a flexible membrane to conform the thermosetcomposite charge to the first smart susceptor surface. The thermosetcomposite charge is heated to a curing temperature using the first smartsusceptor surface.

The features and functions can be achieved independently in variousembodiments of the present disclosure or may be combined in yet otherembodiments in which further details can be seen with reference to thefollowing description and drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

The novel features believed characteristic of the illustrativeembodiments are set forth in the appended claims. The illustrativeembodiments, however, as well as a preferred mode of use, furtherobjectives and features thereof, will best be understood by reference tothe following detailed description of an illustrative embodiment of thepresent disclosure when read in conjunction with the accompanyingdrawings, wherein:

FIG. 1 is an illustration of a block diagram of a manufacturingenvironment in accordance with an illustrative embodiment;

FIG. 2 is an illustration of an isometric view of a manufacturingenvironment with an induction system for forming and curing thermosetcomposite charges in accordance with an illustrative embodiment;

FIG. 3 is an illustration of a cross-sectional view of an inductionsystem for forming and curing thermoset composite charges in accordancewith an illustrative embodiment;

FIG. 4 is an illustration of a cross-sectional view of an inductionsystem for forming and curing thermoset composite charges in accordancewith an illustrative embodiment;

FIG. 5 is an illustration of a cross-sectional view of an inductionsystem for forming and curing thermoset composite charges in accordancewith an illustrative embodiment;

FIG. 6 is an illustration of a pressure versus time chart of forming andcuring a thermoset composite charge in an induction system in accordancewith an illustrative embodiment;

FIG. 7 is an illustration of a temperature versus time chart of formingand curing a thermoset composite charge in an induction system inaccordance with an illustrative embodiment;

FIG. 8 is an illustration of a flowchart of a process for forming andcuring a thermoset composite charge in accordance with an illustrativeembodiment;

FIG. 9 is an illustration of an aircraft manufacturing and servicemethod in the form of a block diagram in accordance with an illustrativeembodiment; and

FIG. 10 is an illustration of an aircraft in the form of a block diagramin which an illustrative embodiment may be implemented.

DETAILED DESCRIPTION

The illustrative embodiments recognize and take into account one or moredifferent considerations. For example, the illustrative embodimentsrecognize and take into account that current processing systems forcomplex small thermoset components require undesirable amounts of laborfor hand lay-up and curing. The illustrative embodiments recognize andtake into account that heated presses/ovens operating at separatetemperatures for forming and curing requires multiple set-ups andprocessing runs.

Referring now to the figures and, in particular, with reference to FIG.1 , an illustration of a block diagram of a manufacturing environment isdepicted in accordance with an illustrative embodiment.

Manufacturing environment 100 includes induction system 102 for formingand curing thermoset composite charge 104. Induction system 102 isconfigured to provide temperature and pressure control for forming andcuring of thermoset composite charge 104.

In one illustrative example, induction system 102 comprises inductiontool 106 and conformable smart susceptor blanket 108 positioned withindie cavity 110 of induction tool 106. Induction tool 106 comprises firsttooling die 112, second tooling die 114, first set of conductors 116,first smart susceptor surface 118, and second smart susceptor surface120. First tooling die 112 and second tooling die 114 are movable withrespect to each other. First tooling die 112 and second tooling die 114comprise a plurality of stacked metal sheets. A plurality of air gaps isdefined between the adjacent stacked metal sheets.

First tooling die 112 comprises plurality of stacked metal sheets 122.Plurality of air gaps 124 are defined between adjacent stacked metalsheets of plurality of stacked metal sheets 122.

Second tooling die 114 comprises plurality of stacked metal sheets 126.Plurality of air gaps 128 are defined between adjacent stacked metalsheets of plurality of stacked metal sheets 126.

First smart susceptor material 130 of first smart susceptor surface 118and second smart susceptor surface 120 has a higher Curie temperaturethan second smart susceptor material 132 in conformable smart susceptorblanket 108. First Curie temperature 134 of first smart susceptormaterial 130 is higher than second Curie temperature 136 of second smartsusceptor material 132.

Conformable smart susceptor blanket 108 comprises second set ofconductors 138 configured to generate second frequency range 140. Insome illustrative examples, second frequency range 140 is 100 kHz-400kHz. In some illustrative examples, second set of conductors 138 issituated to generate a magnetic field cancels out over a short distance.In these illustrative examples, second set of conductors 138 generatingsecond frequency range 140 will not appreciably affect first smartsusceptor surface 118 and second smart susceptor surface 120.

In some illustrative examples, second frequency range 140 and firstfrequency range 142 of first set of conductors 116 may have overlappingfrequencies. In these illustrative examples, second Curie temperature136 of second smart susceptor material 132 protects second smartsusceptor material 132 from overheating.

In some illustrative examples, second frequency range 140 is separatefrom first frequency range 142 of first set of conductors 116. Firstfrequency range 142 and second frequency range 140 may be separated by agap. In some illustrative examples, first frequency range 142 may be 120Hz-1300 Hz while second frequency range 140 is 100 kHz-400 kHz.

In some illustrative examples, second set of conductors 138 are orientedat different angles than first set of conductors 116. In someillustrative examples, second set of conductors 138 are oriented at 90degrees (orthogonal) relative to first set of conductors 116. In someillustrative examples, second set of conductors 138 are oriented at 90degrees (orthogonal) relative to first set of conductors 116 and used ata different frequency. In some illustrative examples, the difference inorientation of a magnetic field of second set of conductors 138 and amagnetic field of first set of conductors 116 allows second set ofconductors 138 to couple well with second smart susceptor material 132,but leave first smart susceptor material 130 relatively alone. In someillustrative examples, the difference in orientation of a magnetic fieldof second set of conductors 138 and a magnetic field of first set ofconductors 116 along with the difference in frequency between firstfrequency range 142 and second frequency range 140 allows second set ofconductors 138 to couple well with second smart susceptor material 132,but leave first smart susceptor material 130 relatively alone.

In these illustrative examples, induction system 102 has first pressureregion 144, second pressure region 146, and third pressure region 148.First pressure region 144 is formed by first smart susceptor surface 118and vacuum film 150. Second pressure region 146 is formed by vacuum film150 and conformable smart susceptor blanket 108. Third pressure region148 is formed by conformable smart susceptor blanket 108 and secondsmart susceptor surface 120.

Each of first pressure region 144, second pressure region 146, and thirdpressure region 148 has an independently controlled pressure. Firstpressure region 144, second pressure region 146, and third pressureregion 148 are controlled to apply desirable pressures to form and thencure thermoset composite charge 104 positioned between vacuum film 150and conformable smart susceptor blanket 108. Although each of firstpressure region 144, second pressure region 146, and third pressureregion 148 is independently controlled, each of first pressure region144, second pressure region 146, and third pressure region 148 iscontrolled in concert to form and cure thermoset composite charge 104.

For example, first pressure region 144 is held at a higher pressure thansecond pressure region 146 and third pressure region 148 during heatingof thermoset composite charge 104 to a forming temperature. As anotherexample, the pressure of third pressure region 148 is increased togreater than first pressure region 144 and second pressure region 146 toform thermoset composite charge 104 against first smart susceptorsurface 118. To form thermoset composite charge 104, the pressure infirst pressure region 144 is reduced. During curing of thermosetcomposite charge 104, pressure in third pressure region 148 is greaterthan the pressures in first pressure region 144 and second pressureregion 146.

In some illustrative examples, induction system 102 includes coolingsystem 152. Cooling system 152 is configured to provide cooling medium154 to a first set of the stacked metal sheets such that the coolingmedium passes through the air gaps between the first set of stackedmetal sheets. For example, cooling system 152 is configured to providecooling medium 154 to plurality of stacked metal sheets 122 such thatcooling medium 154 passes through plurality of air gaps 124 of pluralityof stacked metal sheets 122. In some illustrative examples, coolingsystem 152 may be used to provide cooling medium 154 to a subset ofplurality of air gaps 124. By controlling the application of coolingmedium 154, cooling system 152 may be used to provide directed coolingto selected portions of first smart susceptor surface 118.

In some illustrative examples, cooling system 152 is configured toprovide cooling medium 154 to plurality of stacked metal sheets 126 suchthat cooling medium 154 passes through plurality of air gaps 128 ofplurality of stacked metal sheets 126. In some illustrative examples,cooling system 152 may be used to provide cooling medium 154 to a subsetof plurality of air gaps 128. By controlling the application of coolingmedium 154, cooling system 152 may be used to provide directed coolingto selected portions of second smart susceptor surface 120.

In some illustrative examples, induction system 102 comprises firsttooling die 112 and second tooling die 114, first smart susceptormaterial 130, second smart susceptor material 132, and flexible membrane155. In these illustrative examples, first tooling die 112 and secondtooling die 114 are movable with respect to each other. First toolingdie 112 and second tooling die 114 form die cavity 110. First toolingdie 112 and second tooling die 114 comprise a plurality of stacked metalsheets, and a plurality of air gaps defined between adjacent stackedmetal sheets.

First smart susceptor material 130 is within die cavity 110 andconnected to first tooling die 112. First smart susceptor material 130has first Curie temperature 134.

Second smart susceptor material 132 is within die cavity 110 andassociated with second tooling die 114. Second smart susceptor material132 has second Curie temperature 136 lower than first Curie temperature134.

Flexible membrane 155 is between second tooling die 114 and first smartsusceptor material 130. Flexible membrane 155 is configured to receivepressure. More specifically, flexible membrane 155 is configured toreceive pressure to form thermoset composite charge 104 against firstsmart susceptor surface 118.

Induction system 102 has first pressure region 144, second pressureregion 146, and third pressure region 148. First pressure region 144 iswithin die cavity 110 and is formed by first smart susceptor material130 and vacuum film 150. Second pressure region 146 is within the diecavity 110 and is formed by vacuum film 150 and flexible membrane 155.Third pressure region 148 is within die cavity 110 and is formed byflexible membrane 155 and tooling surface 162 connected to secondtooling die 114.

Induction system 102 comprises first set of conductors 116 and secondset of conductors 138. First set of conductors 116 generates firstfrequency range 142. First smart susceptor material 130 is configured tobe heated by first frequency range 142. In some illustrative examples,first set of conductors 116 is a first set of induction coils extendingthrough first tooling die 112 and second tooling die 114. In otherillustrative examples, first set of conductors 116 could be a number oflarge beds placed inside die cavity 110 of induction tool 106. It ismore energy efficient to have first set of conductors 116 closer tofirst smart susceptor surface 118 and second smart susceptor surface120. When first set of conductors 116 is a number of large beds, it maybe possible to remove first set of conductors 116 and place them into adifferent induction tool other than induction tool 106.

Second set of conductors 138 generates second frequency range 140.Second smart susceptor material 132 is configured to be heated by secondfrequency range 140. In some illustrative examples, when second smartsusceptor material 132 is part of conformable smart susceptor blanket108, second set of conductors 138 may take the form of conductivethreads. In some illustrative examples, second set of conductors 138 maybe a second plurality of induction coils. In some illustrative examples,second set of conductors 138 may be incorporated into flexible membrane155. In some illustrative examples, conformable smart susceptor blanket108 includes second smart susceptor material 132 wrapped in a spiralaround second set of conductors 138 in the form of a litz wire. In theseillustrative examples, the material and pattern of second set ofconductors 138 and second smart susceptor material 132 affects theflexibility of conformable smart susceptor blanket 108. In theseillustrative examples, the material and pattern of second set ofconductors 138 and second smart susceptor material 132 affects thedegree to which conformable smart susceptor blanket 108 stretches.

Second smart susceptor material 132 can be incorporated into anydesirable format. In some illustrative examples, second smart susceptormaterial 132 is a component of conformable smart susceptor blanket 108positioned within die cavity 110. In some illustrative examples,conformable smart susceptor blanket 108 further comprises flexiblemembrane 155. When conformable smart susceptor blanket 108 comprisesflexible membrane 155, pressure is applied to conformable smartsusceptor blanket 108 to form thermoset composite charge 104 to firstsmart susceptor surface 118.

In some other illustrative examples, second smart susceptor material 132is smart susceptor plate 156 beneath flexible membrane 155. In theseillustrative examples, smart susceptor plate 156 is used to heatthermoset composite charge 104 prior to forming thermoset compositecharge 104 to first smart susceptor surface 118 using separate flexiblemembrane 155.

In some illustrative examples, first smart susceptor material 130 ispart of tooling surface 158 with smart susceptor circuits 160 embeddedin tooling surface 158. Tooling surface 158 is connected to firsttooling die 112. Tooling surface 158 may also be referred to as a firsttooling surface. In some illustrative examples, first smart susceptormaterial 130 is part of tooling surface 162 with smart susceptorcircuits 164 embedded in tooling surface 162. Tooling surface 162 isconnected to second tooling die 114. Tooling surface 162 may also bereferred to as a second tooling surface.

In some illustrative examples, smart susceptor circuits 160 and smartsusceptor circuits 164 include first smart susceptor material 130 andfirst set of conductors 116. In some illustrative examples, smartsusceptor circuits 160 and smart susceptor circuits 164 include onlyfirst smart susceptor material 130.

As depicted, first smart susceptor material 130 connected to firsttooling die 112 is part of a first tooling surface, tooling surface 158,connected to first tooling die 112. A second tooling surface, toolingsurface 162, is connected to second tooling die 114. The second toolingsurface, tooling surface 162, comprises first smart susceptor material130.

First smart susceptor material 130 and second smart susceptor material132 are used to heat thermoset composite charge 104. First, at least oneof first smart susceptor material 130 or second smart susceptor material132 are used to heat thermoset composite charge 104 to a formingtemperature.

In some illustrative examples, second smart susceptor material 132 isused to heat thermoset composite charge 104 to a forming temperature. Insome illustrative examples, both first smart susceptor material 130 andsecond smart susceptor material 132 are used to heat thermoset compositecharge 104. In some illustrative examples, second smart susceptormaterial 132 is used to heat at least a portion of thermoset compositecharge 104 while first smart susceptor material 130 is used to heat diecavity 110. In some illustrative examples, second smart susceptormaterial 132 is used to heat first side 166 of thermoset compositecharge 104 that faces the second smart susceptor material 132 whilefirst smart susceptor material 130 is used to heat die cavity 110.

After heating thermoset composite charge 104 to a forming temperature,thermoset composite charge 104 is moved towards first smart susceptormaterial 130. First smart susceptor material 130 is used to heatthermoset composite charge 104 to a curing temperature. Thermosetcomposite charge 104 is held at the curing temperature for a desiredperiod of time. At least one of first smart susceptor material 130 orcooling system 152 are used to maintain thermoset composite charge 104at the curing temperature. Afterwards, at least one of first smartsusceptor material 130, second smart susceptor material 132, or coolingsystem 152 are used to cool thermoset composite charge 104 in acontrolled fashion.

The illustration of manufacturing environment 100 in FIG. 1 is not meantto imply physical or architectural limitations to the manner in which anillustrative embodiment may be implemented. Other components in additionto or in place of the ones illustrated may be used. Some components maybe unnecessary. Also, the blocks are presented to illustrate somefunctional components. One or more of these blocks may be combined,divided, or combined and divided into different blocks when implementedin an illustrative embodiment.

For example, in some illustrative examples, second smart susceptormaterial 132 is present in flexible membrane 155 while second set ofconductors 138 is outside of flexible membrane 155. When second set ofconductors 138 is present outside of flexible membrane 155, flexiblemembrane 155 may have increased flexibility. In some illustrativeexamples, when second set of conductors 138 is outside of flexiblemembrane 155, second smart susceptor material 132 is discontinuouswithin flexible membrane 155. Having second smart susceptor material 132discontinuous with flexible membrane may increase the flexibility offlexible membrane 155.

When the second set of conductors 138 is outside of flexible membrane155, first smart susceptor material 130 and second smart susceptormaterial 132 operate independently due to at least one of design ofsecond set of conductors 138 or shape of second smart susceptor material132. In some illustrative examples, the skin effect may be used toselectively heat large susceptors over small susceptors. In someillustrative examples in which second smart susceptor material 132 issmall, when first frequency range 142 is a low frequency (120-3,000 Hz),first set of conductors 116 would not couple well with second smartsusceptor material 132. In these illustrative examples, the magneticfield from first set of conductors 116 would selectively couple withfirst smart susceptor material 130. When second frequency range 140 forsecond set of conductors 138 is a high frequency (100-400 kHz), secondsmart susceptor material 132 will couple. In some of these illustrativeexamples, first smart susceptor material 130 may also couple to secondfrequency range 140. At least one of geometry of second smart susceptormaterial 132 or wave guides may be used to selectively couple second setof conductors 138 to second smart susceptor material 132.

In some illustrative examples, geometry of second smart susceptormaterial 132 is used to selectively heat small susceptors over largesusceptors. For example, second set of conductors 138 may be arranged toconcentrate a magnetic field from second set of conductors 138 intoflexible membrane 155 using at least one of geometry or wave guides. Insome illustrative examples, second smart susceptor material 132 may beshaped to couple with a magnetic field generated by second set ofconductors 138.

Turning now to FIG. 2 , an illustration of an isometric view of amanufacturing environment with an induction system for forming andcuring thermoset composite charges is depicted in accordance with anillustrative embodiment. Manufacturing environment 200 is a physicalimplementation of manufacturing environment 100 of FIG. 1 .

Thermoset composite charge 202 is present on layup tool 204 inmanufacturing environment 200. As depicted, thermoset composite charge202 is substantially flat.

Layup tool 204 may be one of a plurality of layup tools for thermosetcomposite charges. When a plurality of layup tools is present, aplurality of thermoset composite charges may be laid up substantiallysimultaneously. Laying up thermoset composite charge 202 on layup tool204 may take less time than laying up a thermoset composite structurewith a complex cross-section on a complex layup mandrel.

Induction system 206 is present in manufacturing environment 200.Induction system 206 is a physical implementation of induction system102 of FIG. 1 . Induction system 206 is configured to both form and curethermoset composite charge 202.

Thermoset composite charge 202 is placed into a die cavity of inductionsystem 206. Induction system 206 forms and then cures thermosetcomposite charge 202. Afterwards, a cured thermoset composite structurewith a complex cross-section is removed from induction system 206.

Induction system 206 may have a smaller footprint than separate formingand curing tools. In some illustrative examples, induction system 206may be smaller than an autoclave. In some illustrative examples,induction system 206 reduces the footprint of manufacturing environment200 dedicated to manufacturing a thermoset composite structure with acomplex cross-section.

In some illustrative examples, operating induction system 206 may takefewer resources than an autoclave. In some illustrative examples,operating induction system 206 may take less processing time thanoperating an autoclave.

Turning now to FIG. 3 , an illustration of a cross-sectional view of aninduction system for forming and curing thermoset composite charges isdepicted in accordance with an illustrative embodiment. Induction system300 is a physical implementation of induction system 102 of FIG. 1 .Induction system 300 may be an implementation of induction system 206 ofFIG. 2 .

Induction system 300 is configured to provide temperature and pressurecontrol for forming and curing of thermoset composite charge 302.Induction system 300 comprises induction tool 304 and conformable smartsusceptor blanket 306.

Induction tool 304 comprises first tooling die 308 and second toolingdie 310, first set of conductors 312, first smart susceptor surface 314,and second smart susceptor surface 316. First tooling die 308 and secondtooling die 310 are movable with respect to each other. First toolingdie 308 and second tooling die 310 comprise a plurality of stacked metalsheets, and a plurality of air gaps defined between adjacent stackedmetal sheets.

First tooling die 308 comprises plurality of stacked metal sheets 318.Plurality of air gaps 320 is defined between adjacent stacked metalsheets of plurality of stacked metal sheets 318.

Second tooling die 310 comprises plurality of stacked metal sheets 322.Plurality of air gaps 324 is defined between adjacent stacked metalsheets of plurality of stacked metal sheets 322.

First set of conductors 312 is configured to generate a first frequencyrange. The first frequency range causes first smart susceptor material325 to generate heat. As depicted, first set of conductors 312 takes theform of first set of induction coils 323 extending through first toolingdie 308 and second tooling die 310.

First smart susceptor surface 314 is connected to first tooling die 308.First smart susceptor surface 314 is formed of first smart susceptormaterial 325. Second smart susceptor surface 316 is connected to secondtooling die 310. Second smart susceptor surface 316 is formed of firstsmart susceptor material 325.

Conformable smart susceptor blanket 306 is positioned within die cavity326 of induction tool 304. Conformable smart susceptor blanket 306includes second smart susceptor material 328. First side 329 ofthermoset composite charge 302 faces second smart susceptor material328. First smart susceptor material 325 has a higher Curie temperaturethan second smart susceptor material 328.

The forming temperature of thermoset composite charge 302 is lower thanthe curing temperature of thermoset composite charge 302. Having twosmart susceptor materials with two different Curie temperatures allowsfor controlled application of heat to thermoset composite charge 302 attwo different temperatures. Second smart susceptor material 328 is usedto control heating of thermoset composite charge 302 to the formingtemperature. The second Curie temperature allows for controlled heatingto the forming temperature.

First smart susceptor material 325 is used to control heating ofthermoset composite charge 302 to the curing temperature. The firstCurie temperature allows for controlled heating to the curingtemperature.

Conformable smart susceptor blanket 306 also has second set ofconductors 330. Second set of conductors 330 are configured to generatea second frequency range separate from the first frequency range offirst set of conductors 312.

To form thermoset composite charge 302, induction system 300 heatsthermoset composite charge 302 to a forming temperature. In someillustrative examples, conformable smart susceptor blanket 306 heatsthermoset composite charge 302 to the forming temperature. In someillustrative examples, first smart susceptor surface 314 and secondsmart susceptor surface 316 are used to heat die cavity 326 in additionto conformable smart susceptor blanket 306 heating thermoset compositecharge 302. In these illustrative examples, first smart susceptorsurface 314 and second smart susceptor surface 316 may be heated to atemperature below the forming temperature.

To cure thermoset composite charge 302, induction system 300 heatsthermoset composite charge 302 to a curing temperature. In someillustrative examples, first smart susceptor surface 314 heats thermosetcomposite charge 302 to the curing temperature. In some illustrativeexamples, first smart susceptor surface 314 heats thermoset compositecharge 302 while cooling system 331 simultaneously cools portions offirst smart susceptor surface 314. For example, thermoset compositecharge 302 may have exothermic curing reactions. The exothermicreactions during curing may heat first smart susceptor surface 314 pastthe first Curie temperature. Cooling system 331 may cool first smartsusceptor surface 314 to below the first Curie temperature.

Induction system 300 has first pressure region 332, second pressureregion 334, and third pressure region 336. First pressure region 332 isformed by first smart susceptor surface 314 and vacuum film 338. Secondpressure region 334 is formed by vacuum film 338 and conformable smartsusceptor blanket 306. Thermoset composite charge 302 is positionedbetween vacuum film 338 and conformable smart susceptor blanket 306.Third pressure region 336 is formed by conformable smart susceptorblanket 306 and second smart susceptor surface 316.

Conformable smart susceptor blanket 306 acts as a flexible membrane.When an increased pressure is introduced to third pressure region 336,conformable smart susceptor blanket 306 applies pressure to thermosetcomposite charge 302 to form thermoset composite charge 302 againstfirst smart susceptor surface 314.

Each of first pressure region 332, second pressure region 334, and thirdpressure region 336 are individually controlled to form and curethermoset composite charge 302. First pressure region 332, secondpressure region 334, and third pressure region 336 work in concert toform and cure thermoset composite charge 302.

The illustration of induction system 300 in FIG. 3 is not meant to implyarchitectural limitations as to the manner in which differentillustrative embodiments may be implemented. For example, first smartsusceptor surface 314 is depicted as a “top” tooling surface. In othernon-depicted illustrative examples, first smart susceptor surface 314 isa “bottom” tooling surface.

As another example, third pressure region 336 may not be formed byconformable smart susceptor blanket 306. In this non-depicted example,third pressure region 336 may be formed by a separate flexible membrane.In this non-depicted example, conformable smart susceptor blanket 306remains stationary.

Turning now to FIG. 4 , an illustration of a cross-sectional view of aninduction system for forming and curing thermoset composite charges isdepicted in accordance with an illustrative embodiment. Induction system400 is a physical implementation of induction system 102 of FIG. 1 .Induction system 400 may be an implementation of induction system 206 ofFIG. 2 .

Induction system 400 is configured to provide temperature and pressurecontrol for forming and curing of thermoset composite charge 402.Induction system 400 comprises induction tool 404 and conformable smartsusceptor blanket 406.

Induction tool 404 comprises first tooling die 408, second tooling die410, first set of conductors 412, tooling surface 414, and secondtooling surface 416. First tooling die 408 and second tooling die 410are movable with respect to each other. First tooling die 408 and secondtooling die 410 comprise a plurality of stacked metal sheets, and aplurality of air gaps defined between adjacent stacked metal sheets.

First tooling die 408 comprises plurality of stacked metal sheets 418.Plurality of air gaps 420 is defined between adjacent stacked metalsheets of plurality of stacked metal sheets 418.

Second tooling die 410 comprises plurality of stacked metal sheets 422.Plurality of air gaps 424 is defined between adjacent stacked metalsheets of plurality of stacked metal sheets 422.

First set of conductors 412 is configured to generate a first frequencyrange. As depicted, first set of conductors 412 takes the form of smartsusceptor circuits 423 extending through first tooling die 408 andsecond tooling die 410.

Tooling surface 414 is connected to first tooling die 408. Toolingsurface 414 has embedded smart susceptor circuits 423. Tooling surface414 has first smart susceptor material 425. Tooling surface 416 isconnected to second tooling die 410. Tooling surface 416 has embeddedsmart susceptor circuits 423. Tooling surface 416 has first smartsusceptor material 425.

Conformable smart susceptor blanket 406 is positioned within die cavity426 of induction tool 404. Conformable smart susceptor blanket 406includes second smart susceptor material 428. First side 429 ofthermoset composite charge 402 faces second smart susceptor material428. First smart susceptor material 425 has a higher Curie temperaturethan second smart susceptor material 428.

The forming temperature of thermoset composite charge 402 is lower thanthe curing temperature of thermoset composite charge 402. Having twosmart susceptor materials with two different Curie temperatures allowsfor controlled application of heat to thermoset composite charge 402 attwo different temperatures. Second smart susceptor material 428 is usedto control heating of thermoset composite charge 402 to the formingtemperature. The second Curie temperature allows for controlled heatingto the forming temperature.

First smart susceptor material 425 is used to control heating ofthermoset composite charge 402 to the curing temperature. The firstCurie temperature allows for controlled heating to the curingtemperature.

Conformable smart susceptor blanket 406 also has second set ofconductors 430. Second set of conductors 430 are configured to generatea second frequency range separate from the first frequency range offirst set of conductors 412.

To form thermoset composite charge 402, induction system 400 heatsthermoset composite charge 402 to a forming temperature. In someillustrative examples, conformable smart susceptor blanket 406 heatsthermoset composite charge 402 to the forming temperature. In someillustrative examples, tooling surface 414 and tooling surface 416 areused to heat die cavity 426 in addition to conformable smart susceptorblanket 406 heating thermoset composite charge 402. In theseillustrative examples, tooling surface 414 and tooling surface 416 maybe heated to a temperature below the forming temperature.

To cure thermoset composite charge 402, induction system 400 heatsthermoset composite charge 402 to a curing temperature. In someillustrative examples, tooling surface 414 heats thermoset compositecharge 402 to the curing temperature. In some illustrative examples,tooling surface 414 heats thermoset composite charge 402 while coolingsystem 431 simultaneously cools portions of tooling surface 414. Forexample, thermoset composite charge 402 may have exothermic curingreactions. The exothermic reactions may heat tooling surface 414 pastthe first Curie temperature. Cooling system 431 may cool tooling surface414 to below the first Curie temperature.

Induction system 400 has first pressure region 432, second pressureregion 434, and third pressure region 436. First pressure region 432 isformed by tooling surface 414 and vacuum film 438. Second pressureregion 434 is formed by vacuum film 438 and conformable smart susceptorblanket 406. Thermoset composite charge 402 is positioned between vacuumfilm 438 and conformable smart susceptor blanket 406. Third pressureregion 436 is formed by conformable smart susceptor blanket 406 andtooling surface 416.

Conformable smart susceptor blanket 406 acts as a flexible membrane.When an increased pressure is introduced to third pressure region 436,conformable smart susceptor blanket 406 applies pressure to thermosetcomposite charge 402 to form thermoset composite charge 402 againsttooling surface 414.

Each of first pressure region 432, second pressure region 434, and thirdpressure region 436 are individually controlled to form and curethermoset composite charge 402. First pressure region 432, secondpressure region 434, and third pressure region 436 work in concert toform and cure thermoset composite charge 402.

The illustration of induction system 400 in FIG. 4 is not meant to implyarchitectural limitations as to the manner in which differentillustrative embodiments may be implemented. For example, toolingsurface 414 is depicted as a “top” tooling surface. In othernon-depicted illustrative examples, tooling surface 414 is a “bottom”tooling surface.

As another example, third pressure region 436 may not be formed byconformable smart susceptor blanket 406. In this non-depicted example,third pressure region 436 may be formed by a separate flexible membrane.In this non-depicted example, conformable smart susceptor blanket 406remains stationary.

As yet another example, conformable smart susceptor blanket 406 is notpresent. In this example, a different structure containing second smartsusceptor material 428 is present. In one non-depicted example, a smartsusceptor plate containing second smart susceptor material 428 may bepresent.

Turning now to FIG. 5 , an illustration of a cross-sectional view of aninduction system for forming and curing thermoset composite charges isdepicted in accordance with an illustrative embodiment. Induction system500 is a physical implementation of induction system 102 of FIG. 1 .Induction system 500 may be an implementation of induction system 206 ofFIG. 2 .

Induction system 500 is configured to provide temperature and pressurecontrol for forming and curing of thermoset composite charge 502.Induction system 500 comprises first tooling die 504 and second toolingdie 506, first smart susceptor material 508, second smart susceptormaterial 510, and flexible membrane 512.

First tooling die 504 and second tooling die 506 are movable withrespect to each other. First tooling die 504 and second tooling die 506form die cavity 514. First tooling die 504 and second tooling die 506comprise a plurality of stacked metal sheets, and a plurality of airgaps defined between adjacent stacked metal sheets.

First tooling die 504 comprises plurality of stacked metal sheets 516.Plurality of air gaps 518 is defined between adjacent stacked metalsheets of plurality of stacked metal sheets 516.

Second tooling die 506 comprises plurality of stacked metal sheets 520.Plurality of air gaps 522 is defined between adjacent stacked metalsheets of plurality of stacked metal sheets 520.

First smart susceptor material 508 is within die cavity 514 and isconnected to first tooling die 504. First smart susceptor material 508connected to first tooling die 504 forms first smart susceptor surface524. First smart susceptor material 508 connected to second tooling die506 forms second smart susceptor surface 526. First smart susceptormaterial 508 has a first Curie temperature.

Second smart susceptor material 510 is within die cavity 514 and isassociated with second tooling die 506. As depicted, second smartsusceptor material 510 takes the form of smart susceptor plate 528.Smart susceptor plate 528 is positioned beneath flexible membrane 512.Smart susceptor plate 528 is positioned between flexible membrane 512and second smart susceptor surface 526. Smart susceptor plate 528 restson second smart susceptor surface 526. Second smart susceptor material510 has a second Curie temperature which is lower than the first Curietemperature.

The forming temperature of thermoset composite charge 502 is lower thanthe curing temperature of thermoset composite charge 502. Having twosmart susceptor materials with two different Curie temperatures allowsfor controlled application of heat to thermoset composite charge 502 attwo different temperatures. Second smart susceptor material 510 is usedto control heating of thermoset composite charge 502 to the formingtemperature. The second Curie temperature allows for controlled heatingto the forming temperature.

First smart susceptor material 508 is used to control heating ofthermoset composite charge 502 to the curing temperature. The firstCurie temperature allows for controlled heating to the curingtemperature.

Flexible membrane 512 is positioned between second tooling die 506 andfirst smart susceptor material 508 connected to first tooling die 504.Flexible membrane 512 is configured to receive pressure.

First set of conductors 530 is configured to generate a first frequencyrange. The first frequency range causes first smart susceptor material508 to generate heat. As depicted, first set of conductors 530 takes theform of first set of induction coils 532 extending through first toolingdie 504 and second tooling die 506.

Second set of conductors 534 generates a second frequency range. Secondsmart susceptor material 510 is configured to be heated by the secondfrequency range.

To form thermoset composite charge 502, induction system 500 heatsthermoset composite charge 502 to a forming temperature. In someillustrative examples, smart susceptor plate 528 heats thermosetcomposite charge 502 to the forming temperature. In some illustrativeexamples, first smart susceptor surface 524 and second smart susceptorsurface 526 are used to heat die cavity 514 in addition to smartsusceptor plate 528 heating thermoset composite charge 502. In theseillustrative examples, first smart susceptor surface 524 and secondsmart susceptor surface 526 may be heated to a temperature below theforming temperature. In these illustrative examples, smart susceptorplate 528 heats first side 529 of thermoset charge 502.

To cure thermoset composite charge 502, induction system 500 heatsthermoset composite charge 502 to a curing temperature. In someillustrative examples, first smart susceptor surface 524 heats thermosetcomposite charge 502 to the curing temperature. In some illustrativeexamples, first smart susceptor surface 524 heats thermoset compositecharge 502 while cooling system 536 simultaneously cools portions offirst smart susceptor surface 524. For example, thermoset compositecharge 502 may have exothermic curing reactions. The exothermicreactions may heat first smart susceptor surface 524 past the firstCurie temperature. Cooling system 536 may cool first smart susceptorsurface 524 to below the first Curie temperature.

Induction system 500 has first pressure region 538, second pressureregion 540, and third pressure region 542. First pressure region 538 isformed by first smart susceptor surface 524 and vacuum film 544. Secondpressure region 540 is formed by vacuum film 544 and flexible membrane512. Thermoset composite charge 502 is positioned between vacuum film544 and flexible membrane 512. Third pressure region 542 is formed byflexible membrane 512 and second smart susceptor surface 526. When anincreased pressure is introduced to third pressure region 542, flexiblemembrane 512 applies pressure to thermoset composite charge 502 to formthermoset composite charge 502 against first smart susceptor surface524.

Each of first pressure region 538, second pressure region 540, and thirdpressure region 542 is individually controlled to form and curethermoset composite charge 502. First pressure region 538, secondpressure region 540, and third pressure region 542 work in concert toform and cure thermoset composite charge 502.

The illustration of induction system 500 in FIG. 5 is not meant to implyarchitectural limitations as to the manner in which differentillustrative embodiments may be implemented. For example, first smartsusceptor surface 524 is depicted as a “top” tooling surface. In othernon-depicted illustrative examples, first smart susceptor surface 524 isa “bottom” tooling surface. As another example, first set of conductors530 may instead be smart susceptor circuits.

Turning now to FIG. 6 , an illustration of a pressure versus time chartof forming and curing a thermoset composite charge in an inductionsystem is depicted in accordance with an illustrative embodiment. Chart600 is an illustrative example of pressures within pressure regions,such as first pressure region 144, second pressure region 146, and thirdpressure region 148, of induction system 102 of FIG. 1 . Chart 600 is anillustrative example of pressures within pressure regions of inductionsystem 206 of FIG. 2 . Chart 600 is an illustrative example of pressureswithin pressure regions, such as first pressure region 332, secondpressure region 334, and third pressure region 336, of induction system300 of FIG. 3 . Chart 600 is an illustrative example of pressures withinpressure regions, such as first pressure region 432, second pressureregion 434, and third pressure region 436, of induction system 400 ofFIG. 4 . Chart 600 is an illustrative example of pressures withinpressure regions, such as first pressure region 538, second pressureregion 540, and third pressure region 542, of induction system 500 ofFIG. 5 .

Chart 600 has x-axis 602 and y-axis 604. X-axis 602 is a representationof time. Y-axis 604 is a representation of pressure. Line 606 isrepresentative of a first pressure region in an induction system. Thefirst pressure zone is within a die cavity of the induction system andis formed by a first smart susceptor material and a vacuum film. Line608 is representative of a second pressure region in the inductionsystem. The second pressure region is within the die cavity and isformed by the vacuum film and a flexible membrane. Line 610 isrepresentative of a third pressure region in the induction system. Thethird pressure region is within the die cavity and is formed by theflexible membrane and a second smart susceptor surface connected to thesecond tooling die of the induction system.

Prior to forming, line 608 and line 610 start below line 606. In thisillustrative example, line 606 begins at pressure 612 while line 608 andline 610 begin at pressure 614. Pressure 614 is less than pressure 612.By starting line 606 at pressure 612 greater than pressure 614, athermoset composite charge between the flexible membrane and the vacuumfilm is encouraged towards the flexible membrane. Line 606 having ahigher pressure than line 608 and line 610 allows the flexible membraneto capture the thermoset composite charge for movement.

In some illustrative examples, line 606 begins at ambient pressure whileline 608 and line 610 begin at vacuum pressure. In some illustrativeexamples, line 608 and line 610 may begin at ambient pressure while line606 is at an elevated pressure.

Forming begins at time 616. At time 616, line 610 begins to increase inpressure. At or slightly after time 616, line 606 decreases in pressure.By increasing the pressure between the flexible membrane and a toolingsurface connected to the second tooling die, represented by line 610,the thermoset composite charge between the flexible membrane and thevacuum film is propelled towards the first smart susceptor material. Bydecreasing the pressure between the first smart susceptor material andthe vacuum film, represented by line 606, gas does not prevent thethermoset composite charge from forming against the first smartsusceptor material.

At time 618, line 610 has reached pressure 620. Pressure 620 is adesired curing pressure. Line 610 is maintained at pressure 620 duringcuring of the thermoset composite charge.

Line 610 is maintained at pressure 620 during a controlled cooldown ofthe thermoset composite charge. After curing and cooling down of thethermoset composite charge, pressure is released from the third pressureregion.

Turning now to FIG. 7 , an illustration of a temperature versus timechart of forming and curing a thermoset composite charge in an inductionsystem is depicted in accordance with an illustrative embodiment. Chart700 is an illustrative example of temperatures of thermoset compositecharge 104 during forming and curing in induction system 102 of FIG. 1 .Chart 700 is an illustrative example of temperatures of a thermosetcomposite charge 202 during forming and curing in induction system 206of FIG. 2 . Chart 700 is an illustrative example of temperatures ofthermoset composite charge 302 during forming and curing in inductionsystem 300 of FIG. 3 . Chart 700 is an illustrative example oftemperatures of thermoset composite charge 402 during forming and curingin induction system 400 of FIG. 4 . Chart 700 is an illustrative exampleof temperatures of thermoset composite charge 502 during forming andcuring in induction system 500 of FIG. 5 . Chart 700 is an illustrativeexample of temperatures of a thermoset composite charge formed and curedusing the pressures shown in chart 600 of FIG. 6 .

Chart 700 has x-axis 702 and y-axis 704. X-axis 702 is a representationof time. Y-axis 704 is a representation of temperature. Line 706 isrepresentative of a temperature of a thermoset composite charge betweena flexible membrane and a vacuum film in an induction system.

Line 706 starts at temperature 708 and heats to temperature 710 by time616. Increasing the temperature of a thermoset composite chargerepresented by line 706 is performed by heating a second smart susceptormaterial within a die cavity of the induction system. The second smartsusceptor material has a second Curie temperature and is configured toheat the thermoset composite charge to temperature 710. In someillustrative examples, a first smart susceptor material having a firstCurie temperature higher than the second Curie temperature may be usedto heat the die cavity of the induction system. In these illustrativeexamples, the first smart susceptor material is heated to a temperaturebelow the forming temperature. Heating the die cavity using the firstsmart susceptor material aids in heating the entirety of the thermosetcomposite charge to the forming temperature.

Forming of the thermoset composite charge by application of pressurebegins at time 616. Forming takes place from time 616 to time 618. Theapplication of pressure during forming can be seen in FIG. 6 betweentime 616 and time 618. During forming, line 706 maintains temperature710 from time 616 to time 618. Temperature 710 may be referred to as aforming temperature.

Following forming, the thermoset composite charge has been shaped to thefirst smart susceptor material. At time 618, the thermoset compositecharge has been shaped to the first smart susceptor material.

At time 618, line 706 starts at temperature 710 and heats to temperature712 by time 714. Increasing the temperature of a thermoset compositecharge represented by line 706 is performed by heating the first smartsusceptor material.

Temperature 712 is a curing temperature for the thermoset compositecharge. Line 706 is maintained at temperature 712 from time 714 to time716. Line 706 is maintained at temperature 712 using the first smartsusceptor material. In some illustrative examples, a cooling system isused to cool the first smart susceptor material if the first smartsusceptor material exceeds a Curie temperature of the first smartsusceptor material. In some illustrative examples, exothermic reactionsof the thermoset composite charge cause the first smart susceptormaterial to locally exceed the Curie temperature. In these illustrativeexamples, a combination of heating using the first smart susceptormaterial and cooling using the cooling system is used to maintain line706 at temperature 712.

The thermoset composite charge is cured from time 714 to 716. At time716, a controlled cooldown of the thermoset composite charge begins. Attime 716, line 706 decreases in temperature from temperature 712 totemperature 708. The controlled cooldown includes the application ofboth heat and cooling to the thermoset composite charge. In someillustrative examples, the controlled cooldown includes simultaneouslycooling the first smart susceptor surface and applying heat using aconformable smart susceptor blanket.

Turning now to FIG. 8 , an illustration of a flowchart of a process forforming and curing a thermoset composite charge is depicted inaccordance with an illustrative embodiment. Method 800 may be used toform and cure thermoset composite charge 104 using induction system 102of FIG. 1 . Method 800 may be used to form and cure thermoset compositecharge 202 using induction system 206 of FIG. 2 . Method 800 may be usedto form and cure thermoset composite charge 302 using induction system300 of FIG. 3 . Method 800 may be used to form and cure thermosetcomposite charge 402 using induction system 400 of FIG. 4 . Method 800may be used to form and cure thermoset composite charge 502 usinginduction system 500 of FIG. 5 .

Method 800 places a thermoset composite charge within a die cavity of aninduction tool, wherein the induction tool comprises a first tooling dieand a second tooling die movable with respect to each other, and whereinthe first tooling die and the second tooling die form the die cavity,the first tooling die and the second tooling die comprising a pluralityof stacked metal sheets, a plurality of air gaps defined betweenadjacent stacked metal sheets (operation 802). Method 800 heats thethermoset composite charge within the die cavity to a formingtemperature using a second smart susceptor material within the diecavity (operation 804). The second smart susceptor material is acomponent of any desirable structure.

In some illustrative examples, the second smart susceptor material is acomponent of a conformable smart susceptor blanket. In otherillustrative examples, the second smart susceptor material is part of asmart susceptor plate. In one illustrative example, the second smartsusceptor material is part of a smart susceptor plate with smartsusceptor circuits.

In some illustrative examples, heating the thermoset composite charge tothe forming temperature comprises heating the thermoset composite chargeusing a conformable smart susceptor blanket positioned within the diecavity, wherein the conformable smart susceptor blanket comprises thesecond smart susceptor material. In some illustrative examples, heatingthe thermoset composite charge within the die cavity to the formingtemperature using the second smart susceptor material comprises heatinga first side of the thermoset composite charge using the second smartsusceptor material, and heating the die cavity using the first smartsusceptor surface. In some illustrative examples, heating the thermosetcomposite charge to the forming temperature comprises generating asecond frequency range using a second set of conductors in theconformable smart susceptor blanket.

Method 800 moves the thermoset composite charge within the die cavitytowards a first smart susceptor surface connected to the first toolingdie after heating the thermoset composite charge to the formingtemperature (operation 806). Method 800 moves the thermoset compositecharge using a flexible membrane. In some illustrative examples, aconformable smart susceptor blanket comprises the flexible membrane. Insome illustrative examples, moving the thermoset composite charge withinthe die cavity comprises increasing a pressure between the conformablesmart susceptor blanket and a second smart susceptor surface connectedto the second tooling die, wherein the conformable smart susceptorblanket comprises the flexible membrane.

Method 800 applies pressure to the thermoset composite charge using aflexible membrane to conform the thermoset composite charge to the firstsmart susceptor surface (operation 808). Method 800 heats the thermosetcomposite charge to a curing temperature using the first smart susceptorsurface (operation 810). Afterwards, the method terminates.

In some illustrative examples, heating the thermoset composite charge tothe curing temperature comprises generating a first frequency rangeusing a first plurality of conductors, wherein the first smart susceptormaterial is configured to be heated by the first frequency range.

The flowcharts and block diagrams in the different depicted embodimentsillustrate the architecture, functionality, and operation of somepossible implementations of apparatus and methods in an illustrativeembodiment. In this regard, each block in the flowcharts or blockdiagrams may represent a module, a segment, a function, and/or a portionof an operation or step.

In some alternative implementations of an illustrative embodiment, thefunction or functions noted in the blocks may occur out of the ordernoted in the figures. For example, in some cases, two blocks shown insuccession may be executed substantially concurrently, or the blocks maysometimes be performed in the reverse order, depending upon thefunctionality involved. Also, other blocks may be added, in addition tothe illustrated blocks, in a flowchart or block diagram.

In some illustrative examples, method 800 further comprises coolingportions of the first smart susceptor surface to below a first Curietemperature of the first smart susceptor surface. In some illustrativeexamples, method 800 further comprises cooling the thermoset compositecharge in a controlled fashion by simultaneously cooling the first smartsusceptor surface using cooling medium flowing through the plurality ofair gaps of the first tooling die and applying heat from the conformablesmart susceptor blanket.

Illustrative embodiments of the present disclosure may be described inthe context of aircraft manufacturing and service method 900 as shown inFIG. 9 and aircraft 1000 as shown in FIG. 10 . Turning first to FIG. 9 ,an illustration of an aircraft manufacturing and service method isdepicted in accordance with an illustrative embodiment. Duringpre-production, aircraft manufacturing and service method 900 mayinclude specification and design 902 of aircraft 1000 in FIG. 10 andmaterial procurement 904.

During production, component and subassembly manufacturing 906 andsystem integration 908 of aircraft 1000 takes place. Thereafter,aircraft 1000 may go through certification and delivery 910 in order tobe placed in service 912. While in service 912 by a customer, aircraft1000 is scheduled for routine maintenance and service 914, which mayinclude modification, reconfiguration, refurbishment, or othermaintenance and service.

Each of the processes of aircraft manufacturing and service method 900may be performed or carried out by a system integrator, a third party,and/or an operator. In these examples, the operator may be a customer.For the purposes of this description, a system integrator may include,without limitation, any number of aircraft manufacturers andmajor-system subcontractors; a third party may include, withoutlimitation, any number of vendors, subcontractors, and suppliers; and anoperator may be an airline, a leasing company, a military entity, aservice organization, and so on.

With reference now to FIG. 10 , an illustration of an aircraft isdepicted in which an illustrative embodiment may be implemented. In thisexample, aircraft 1000 is produced by aircraft manufacturing and servicemethod 900 of FIG. 9 and may include airframe 1002 with plurality ofsystems 1004 and interior 1006. Examples of systems 1004 include one ormore of propulsion system 1008, electrical system 1010, hydraulic system1012, and environmental system 1014. Any number of other systems may beincluded. Although an aerospace example is shown, different illustrativeembodiments may be applied to other industries, such as the automotiveindustry.

Apparatuses and methods embodied herein may be employed during at leastone of the stages of aircraft manufacturing and service method 900. Oneor more illustrative embodiments may be used during at least one ofcomponent and subassembly manufacturing 906, system integration 908, ormaintenance and service 914 of FIG. 9 . For example, induction system102 of FIG. 1 may be used during component and subassembly manufacturing906 to form and cure thermoset composite charge 104. Thermoset compositecharge 104 of FIG. 1 may be formed and cured during component andsubassembly manufacturing 906 using method 800 of FIG. 8 .

As used herein, the phrase “at least one of,” when used with a list ofitems, means different combinations of one or more of the listed itemsmay be used, and only one of each item in the list may be needed. Inother words, “at least one of” means any combination of items and numberof items may be used from the list, but not all of the items in the listare required. The item may be a particular object, a thing, or acategory.

For example, “at least one of item A, item B, or item C” may include,without limitation, item A, item A and item B, or item B. This examplealso may include item A, item B, and item C, or item B and item C. Ofcourse, any combination of these items may be present. In otherexamples, “at least one of” may be, for example, without limitation, twoof item A, one of item B, and ten of item C; four of item B and seven ofitem C; or other suitable combinations.

Thermoset composite charge 104 of FIG. 1 may be a formed and cured intoa component of aircraft 1000 joined during system integration 908.Induction system 102 of FIG. 1 may be used to form replacementcomponents used during maintenance and service 914 of FIG. 9 . Forexample, induction system 102 of FIG. 1 may be used to create compositestructure from thermoset composite charge 104 to form a replacementcomponent used during maintenance and service 914 of FIG. 9 . Thermosetcomposite charge 104 of FIG. 1 may be formed and cured into a componentfor at least one of airframe 1002 or interior 1006.

The illustrative examples provide a first smart susceptor material and asecond smart susceptor material to form and cure a thermoset compositecharge in an induction system. Both forming and curing in a singleinduction system may reduce at least one of overall tooling costs,tooling footprint, manufacturing time, manufacturing utilities, ormanufacturing waste. For example, forming and curing using inductionheating may use less energy than curing in an autoclave. As anotherexample, forming and curing using a single induction system may reducematerial waste from bagging and rebagging a thermoset composite chargefor separate forming and curing steps.

In some illustrative examples, the induction system combines the use ofa flexible smart susceptor blanket style heater with an inductivelyheated laminated tool using smart susceptor shells. In theseillustrative examples, the conformable smart susceptor blanket is heatedto the optimal forming temperature and the lay-up is formed against thesurface of the laminated tool using pneumatic pressure against aflexible membrane. In some illustrative examples, the conformable smartsusceptor blanket is the flexible membrane. In other illustrativeexamples, a separate flexible membrane is provided for applyingpneumatic pressure.

The laminated tooling is then rapidly heated to the curing temperatureand the charge is cured. This process enables the forming of initialflat or simply shaped charges into more complicated cure parts in aseamlessly combined forming and curing step. This process uses the quicklay-up of simple shapes along with the efficient and rapid forming andcuring using less labor for improved affordability.

The description of the different illustrative embodiments has beenpresented for purposes of illustration and description, and is notintended to be exhaustive or limited to the embodiments in the formdisclosed. Many modifications and variations will be apparent to thoseof ordinary skill in the art. Further, different illustrativeembodiments may provide different features as compared to otherillustrative embodiments. The embodiment or embodiments selected arechosen and described in order to best explain the principles of theembodiments, the practical application, and to enable others of ordinaryskill in the art to understand the disclosure for various embodimentswith various modifications as are suited to the particular usecontemplated.

What is claimed is:
 1. An induction system configured to providetemperature and pressure control for forming and curing of a thermosetcomposite charge, the induction system comprising: a first tooling dieand a second tooling die movable with respect to each other, wherein thefirst tooling die and the second tooling die form a die cavity, thefirst tooling die and the second tooling die comprising a plurality ofstacked metal sheets, a plurality of air gaps defined between adjacentstacked metal sheets; a first smart susceptor material within the diecavity and connected to the first tooling die, wherein the first smartsusceptor material has a first Curie temperature; a second smartsusceptor material within the die cavity and associated with the secondtooling die, wherein the second smart susceptor material has a secondCurie temperature lower than the first Curie temperature; a flexiblemembrane between the second tooling die and the first smart susceptormaterial, wherein the flexible membrane is configured to receivepressure; a first pressure region within the die cavity formed by thefirst smart susceptor material and a vacuum film; a second pressureregion within the die cavity formed by the vacuum film and the flexiblemembrane; and a third pressure region formed by the flexible membraneand a tooling surface connected to the second tooling die.
 2. Theinduction system of claim 1 further comprising: a first set ofconductors extending through the first tooling die and the secondtooling die generating a first frequency range, wherein the first smartsusceptor material is configured to be heated by the first frequencyrange; and a second set of conductors generating a second frequencyrange, wherein the second smart susceptor material is configured to beheated by the second frequency range.
 3. The induction system of claim1, wherein the second smart susceptor material is a component of aconformable smart susceptor blanket positioned within the die cavity. 4.The induction system of claim 1, wherein the second smart susceptormaterial is a smart susceptor plate beneath the flexible membrane. 5.The induction system of claim 1 further comprising: a cooling systemconfigured to provide a cooling medium to a first set of stacked metalsheets such that the cooling medium passes through the air gaps betweenthe first set of stacked metal sheets.
 6. The induction system of claim1, wherein the first smart susceptor material is part of a toolingsurface with smart susceptor circuits embedded in the tooling surface,and wherein the tooling surface is connected to the first tooling die.7. The induction system of claim 1, wherein the first smart susceptormaterial connected to the first tooling die is part of a first toolingsurface connected to the first tooling die, and the induction systemfurther comprises: a second tooling surface connected to the secondtooling die, wherein the second tooling surface comprises the secondsmart susceptor material.
 8. An induction system configured to providetemperature and pressure control for forming and curing of a thermosetcomposite charge, the induction system comprising: a first tooling dieand a second tooling die movable with respect to each other, wherein thefirst tooling die and the second tooling die form a die cavity, thefirst tooling die and the second tooling die comprising a plurality ofstacked metal sheets, a plurality of air gaps defined between adjacentstacked metal sheets; a first smart susceptor material within the diecavity and connected to the first tooling die, wherein the first smartsusceptor material has a first Curie temperature; a second smartsusceptor material within the die cavity and associated with the secondtooling die, wherein the second smart susceptor material has a secondCurie temperature lower than the first Curie temperature; and a flexiblemembrane between the second tooling die and the first smart susceptormaterial, wherein the flexible membrane is configured to receivepressure, wherein the second smart susceptor material is a component ofa conformable smart susceptor blanket positioned within the die cavity,wherein the conformable smart susceptor blanket further comprises theflexible membrane.
 9. An induction system configured to providetemperature and pressure control for forming and curing of a thermosetcomposite charge, the induction system comprising: an induction toolcomprising: a first tooling die and a second tooling die movable withrespect to each other, the first tooling die and the second tooling diecomprising a plurality of stacked metal sheets, a plurality of air gapsdefined between adjacent stacked metal sheets; a first set ofconductors; a first smart susceptor surface connected to the firsttooling die; and a second smart susceptor surface connected to thesecond tooling die; a conformable smart susceptor blanket positionedwithin a die cavity of the induction tool; a first pressure regionformed by the first smart susceptor surface and a vacuum film; a secondpressure region formed by the vacuum film and the conformable smartsusceptor blanket; and a third pressure region formed by the conformablesmart susceptor blanket and the second smart susceptor surface.
 10. Theinduction system of claim 9, wherein the first smart susceptor surfaceis part of a tooling surface with smart susceptor circuits embedded inthe tooling surface, and wherein the tooling surface is connected to thefirst tooling die.
 11. The induction system of claim 9, furthercomprising: wherein the second smart susceptor surface is configured toheat a thermoset charge to a forming temperature, and wherein the firstsmart susceptor surface is configured to heat the thermoset charge to acuring temperature.
 12. The induction system of claim 9, furthercomprising: a cooling system configured to cool portions of the firstsmart susceptor surface to below a first Curie temperature of the firstsmart susceptor surface.
 13. An induction system configured to providetemperature and pressure control for forming and curing of a thermosetcomposite charge, the induction system comprising: an induction toolcomprising: a first tooling die and a second tooling die movable withrespect to each other, the first tooling die and the second tooling diecomprising a plurality of stacked metal sheets, a plurality of air gapsdefined between adjacent stacked metal sheets; a first set ofconductors; a first smart susceptor surface connected to the firsttooling die; and a second smart susceptor surface connected to thesecond tooling die; and a conformable smart susceptor blanket positionedwithin a die cavity of the induction tool, wherein a first smartsusceptor material of the first smart susceptor surface and the secondsmart susceptor surface has a higher Curie temperature than a secondsmart susceptor material in the conformable smart susceptor blanket. 14.An induction system configured to provide temperature and pressurecontrol for forming and curing of a thermoset composite charge, theinduction system comprising: an induction tool comprising: a firsttooling die and a second tooling die movable with respect to each other,the first tooling die and the second tooling die comprising a pluralityof stacked metal sheets, a plurality of air gaps defined betweenadjacent stacked metal sheets; a first set of conductors; a first smartsusceptor surface connected to the first tooling die; and a second smartsusceptor surface connected to the second tooling die; and a conformablesmart susceptor blanket positioned within a die cavity of the inductiontool, wherein the conformable smart susceptor blanket comprises a secondset of conductors configured to generate a second frequency rangeseparate from a first frequency range of the first set of conductors.15. An induction system configured to provide temperature and pressurecontrol for forming and curing of a thermoset composite charge, theinduction system comprising: a first tooling die and a second toolingdie movable with respect to each other, wherein the first tooling dieand the second tooling die form a die cavity, the first tooling die andthe second tooling die comprising a plurality of stacked metal sheets, aplurality of air gaps defined between adjacent stacked metal sheets; afirst smart susceptor surface formed of a first smart susceptor materialwithin the die cavity and connected to the first tooling die; a secondsmart susceptor surface formed of a second smart susceptor materialwithin the die cavity and associated with the second tooling die; and aflexible membrane between the second tooling die and the first smartsusceptor material, wherein the flexible membrane is configured toreceive pressure to move a thermoset charge within the die cavity andapply pressure to the thermoset charge to conform the thermoset chargeto the first smart susceptor surface, wherein the second smart susceptormaterial is a component of a conformable smart susceptor blanketpositioned within the die cavity.
 16. The induction system of claim 15further comprising: wherein the second smart susceptor surface isconfigured to heat a thermoset charge to a forming temperature, andwherein the first smart susceptor surface is configured to heat thethermoset charge to a curing temperature.
 17. The induction system ofclaim 15, wherein the first smart susceptor material of the first smartsusceptor surface has a higher Curie temperature than the second smartsusceptor material.
 18. The induction system of claim 15, wherein thefirst smart susceptor material is configured to be heated by a firstfrequency range, wherein the second smart susceptor material isconfigured to be heated by a second frequency range separate from thefirst frequency range.
 19. The induction system of claim 15 furthercomprising: a cooling system configured to cool portions of the firstsmart susceptor surface to below a first Curie temperature of the firstsmart susceptor surface.
 20. The induction system of claim 15, whereinthe conformable smart susceptor blanket further comprises the flexiblemembrane.
 21. The induction system of claim 15, wherein the first smartsusceptor material is part of a tooling surface with smart susceptorcircuits embedded in the tooling surface, and wherein the toolingsurface is connected to the first tooling die.